Salokhe, V.M., Gee-Clough, D., Tamtomo, P.
Accelerated wear testing of enamel coated mild steel rings was conducted to investigate wear characteristics relative to those of uncoated mild steel rings. The tests were conducted in sandy soil and on sand papers of silicone carbide. Results of the studies were expressed in terms of weight loss and wear rate in relation to the test duration. It was observed that over a period of 120 h of testing in sandy soil, the amounts of wear of enamel coated rings and the uncoated mild steel rings were almost the same. The tests on sand papers showed that enamel coated rings wore faster than the mild steel rings. The rate of wear of the enamel coated rings, however, was not so high as to render the process impractical for use in improving the performance of soil-engaging devices used in agriculture.
Pengujian keausan yang dipercepat dari cincin baja ringan dilapisi enamel dilakukan untuk mengetahui karakteristik keausan dibandingkan dengan cincin baja ringan yang tidak dilapisi. Pengujian dilakukan di tanah berpasir dan pada kertas pasir silikon karbida. Hasil penelitian dinyatakan dalam bentuk penurunan berat dan tingkat keausan yang terkait dengan durasi tes. Telah diamati bahwa dalam waktu 120 jam pengujian di tanah berpasir, jumlah pemakaian cincin dilapisi enamel dan cincin baja ringan yang tidak dilapisi hampir sama. Pengujian pada kertas pasir menunjukkan bahwa cincin terlapiskan enamel lebih cepat aus dari pada cincin baja ringan. Bagaimanapun tingkat pemakaian cincin dilapisi enamel tidak begitu tinggi sehingga proses pembuatannya tidak praktis untuk digunakan dalam meningkatkan kinerja alat pengikat tanah yang digunakan di bidang/sektor pertanian.